Optical characterization of Cu2ZnSnS4 nanocrystals thin film
Yükleniyor...
Dosyalar
Tarih
2016
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Springer
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
Synthesis of nanostructured powders of tetragonal Cu2ZnSnS4 (CZTS) nanocrystals was carried out based on the hot-injection process. High-quality CZTS thin films were prepared by spin coating method onto the Corning 1737 glass substrates. CZTS nanoparticles were characterized using X-ray diffraction (XRD), small-angle X-ray scattering (SAXS), transmission electron microscopy (TEM) and high resolution TEM. It is observed that a good quality CZTS film can be obtained by spin deposition at room temperature. The optical properties of the film were studied using UV-visible spectra between 300 and 1000 nm wavelength range. The direct optical band gap of the film evolved as 1.49 eV. This value is close to the ideal band gap for highest theoretical conversion efficiency of solar cell. The optical absorption coefficients of the film between 300 and 1000 nm are found to be about 2 and 7.6 x 10(4) cm(-1), respectively. The optical dispersion parameters of the film were also determined by Wemple-DiDomenico single oscillator model.
Açıklama
WOS:000384418600021
Anahtar Kelimeler
Kaynak
WoS Q Değeri
Q2
Scopus Q Değeri
Q2
Cilt
27
Sayı
10
Künye
Kişnişci, Z., Özel, F., Yüksel, O. F., Tuğluoğlu, N. (2016). Optical characterization of Cu2ZnSnS4 nanocrystals thin film. Journal of Materials Science: Materials in Electronics, 27, 10, 10128-10135.